ER316L
AWS A5.9 ER316L
EN ISO 14343-A : W 19 12 3 L
Description：
A super low carbon and high silicon stainless steel welding wire has high deposition efficiency, used to weld 19%Cr12%Ni2%Mo and similar stainless steels. The low carbon content to help prevent intergranular corrosion and higher silicon increase weld puddle fluidity, suitable for high speed welding. Used to weld 19%Cr13%Ni2%Mo and similar stainless steels, like food and Beverage, Petrochemical plants, Pulp and Paper, other general fabrication on stainless steels.
Diameters:
0.8mm,0.9mm,1.0mm,1.2mm.
Typical Mechanical Properties:
Tensile strength(MPa): | 530 |
Yield stress(MPa): | 410 |
Elongation(%): | 42 |
Typical Chemical Properties:
C | Mn | P | S | Si | Ni | Cr | Mo | Cu |
0.02 | 1.9 | 0.012 | 0.008 | 0.85 | 13.0 | 19.0 | 2.6 | 0.015 |
Welding Current:(AC/DC+)
Diameter(mm) | 0.8 | 0.9 | 1.0 | 1.2 | |
Current/A | 55-160 | 65-220 | 80-240 | 100-300 | |
Voltage/V | 15-24 | 15-28 | 15-28 | 15-29 | |
Note:
1.Rusty, oil stains, water and other impurity on the weld parts must be cleaned before welding.
2.Shield Gas:Ar+0.5-5%CO2 or Ar+0.5-3%O2.
3.Gas speed:20-25L/Min
4.DC+ connection; Arc length:4-6mm.
5. Tig rods ER316LSi 1.6mm, 2.0mm, 2.4mm, 3.2mm available