E308LT0-3
AWS A5.22 E308LT0-3
Description：
It is self-shield, flux cored, stainless steel wire is designed with a nominal weld metal composition of 21% chromium and 10% nickel with a maximum carbon content of .03%. The low carbon in E308LT0-3 minimizes carbide precipitation and makes the weld metal more resistant to intergranular corrosion.
Diameters:
0.9mm, 1.0mm, 1.2mm
Typical Mechanical Properties:
Tensile strength(MPa): | 585 |
Yield stress(MPa): | -- |
Elongation(%): | 43 |
Typical Chemical Properties:
C | Mn | P | S | Si | Ni | Cr | Mo | Cu |
0.035 | 1.60 | 0.020 | 0.015 | 0.60 | 9.5 | 20.3 | 0.01 | 0.02 |
Welding Current:(DC+)
Diameter(mm) | 1.2 | 1.6 | |
Current/A | 120-220 | 180-300 | |
Voltage/V | 20-32 | 20-32 | |
Gas speed/(L/Min | 20-25 | 20-25 | |
Note:
1.Shield gas: none
2. Preheat before welding.
3. Interpass temperature: ≤80℃