Description：
E316LT0-3 is a self-shielded, flux cored, stainless steel wire designed with a nominal weld metal composition of 19% chromium, 12.5% nickel, 2.5% molybdenum and a maximum carbon content of 0.03%. The Mo contained improves resistance to pitting and provides increased creep resistance. In addition, the low carbon content minimizes carbide precipitation and makes it more resistant to intergranular corrosion.
Diameters:
0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Typical Mechanical Properties:
Tensile strength(MPa): | 544 |
Yield stress(MPa): | -- |
Elongation(%): | 42 |
Impact values(≥27J/-196℃): | 49 |
Typical Chemical Properties:
C | Mn | P | S | Si | Ni | Cr | Mo | Cu |
0.039 | 1.4 | 0.022 | 0.007 | 0.55 | 12.30 | 18.50 | 2.60 | 0.03 |
Welding Current:(DC+)
Diameter(mm) | 1.2 | 1.6 | |
Current/A | 120-220 | 180-300 | |
Voltage/V | 20-32 | 20-32 | |
Gas speed/(L/Min | 20-25 | 20-25 | |
Note:
1.Shield gas: none
2. Preheat before welding.
3. Interpass temperature: ≤80℃