E2209-16
AWS A5.4 E2209-16
ISO3581-A-E19 9 Nb R
GB/T 983 E2209-16
Description:
E2209-16 is used to weld duplex stainless steels such as UNS Number N3 1803. The welds offer excellent resistance to stress, corrosion, cracking, and pitting. The micro-structure of the weld metal consists of austenite and ferrite, and the ferrite of weld metal will be lower than the ferrite of type 2205 base metal. When welding of duplex stainless steel, controlled parameters must be used to achieve specified mechanical and corrosion resistance properties.
Diameters:
2.5mm, 3.2mm, 4.0mm, 5.0mm.
Typical Mechanical Properties:
Tensile strength(MPa): | 610 |
Yield stress(MPa): | -- |
Elongation(%): | 38 |
Typical Chemical Properties:
C | Mn | P | S | Si | Ni | Cr | Nb | Cu |
0.051 | 0.85 | 0.025 | 0.003 | 0.68 | 9.6 | 19.8 | 0.35 | 0.15 |
Welding Current:(AC/DC±)
Diameter(mm) | 2.5 | 3.2 | 4.0 | 5.0 | |
Current/A | F/H | 60-90 | 80-120 | 100-140 | 150-210 |
Current/A | V/OH | 40-70 | 60-100 | 80-140 | -- |
Note:
1.The electrodes should be baked 1 hours in 300-350℃ before using.
2.Welding in short arc,and swing scope should not excess 2.5 times of the electrode diameter.